NiAl95/5 Thermal Spray Wire
Ni-Al Arc Spray wire for bond coats and one-step restoration, reported with about 93% Ni rather than a composition inferred from the 95/5 name.
Thermal spray wires
45CT Spray Wire
Ni-Cr-Ti 45CT wire for protecting boiler water-wall tubes and fan blades against high-temperature corrosion, oxidation and sulfidation.
Published coating strength of 48 MPa
Published coating hardness of 45 HRC
Source lists Ni, Cr and Ti without percentages
Product description
45CT Spray Wire is maintained as a separate record from the NiCrTi 45CT page. Its source lists Ni, Cr and Ti without percentages, so composition values are not imported from the other product. Directly published figures are 48 MPa coating strength, 45 HRC coating hardness and a material melting temperature of 1,450°C.
Published applications focus on boiler water-wall tubes and fan blades exposed to high-temperature corrosion, oxidation and sulfidation. The page gives no diameter, package, spray process or surface preparation. Wrought-material statements at 1,800°F, the two-mils-per-year figure and an undated 24-month field statement are excluded as coating guarantees.
Protects only the two source-listed components, boiler water-wall tubes and fan blades, against high-temperature corrosion, oxidation and sulfidation; no other equipment application is asserted.
Technical specifications
- Listed elements
- Ni, Cr, Ti; percentages not published
- Coating strength
- 48 MPa
- Coating hardness
- 45 HRC
- Material melting temperature
- 1450 °C
- Diameter and packaging
- N/A
- Process and surface preparation
- N/A
Related products
NiCrTi 45CT Thermal Spray Wire
NiCrTi 45CT wire for protecting boiler tubes against sulfidation and sulfur-vanadium atmospheres; the source does not identify the operating spray process.
SS420 Thermal Spray Wire
Martensitic SS420 wire for Arc Spray deposits with high hardness, strong bonding, low shrinkage and suitability for wear-resistant dimensional repair.
Zinc Wire Spray
High-purity zinc wire for sacrificial-anode protection of steel in atmospheric and seawater service; the published assay contains no aluminium.